Wire

Name

Material

Approved Specs

Diameter/

Weight

Dây nhôm kẽm

21E Zinc/15% Aluminium

This data sheet is offered as guidance for our standard range of products. Additional product variants and technical information, Including MSDS sheets, are available from Metallisation

EN ISO 14919:2015-2.3-xx-1

1.6mm/15kg 3.2mm/200kg 4.0mm/200kg

24E Zinc Alloy Moulding Wire

This data sheet is offered as guidance for our standard range of products. Additional product variants and technical information, Including MSDS sheets, are available from Metallisation

1.6mm/15kg

27E Aluminium/Zinc 95/5

Commonly used for corrosion protection of welded high-grade aluminium.

2.0mm/6kg

Molypden

99E Molybdenum

1.6mm/10kg

70E Monel (30% Nickel)

Used for its sea water corrosion resistance and machine element work in this environment.

1.6mm/13.6kg

71E Monel (67% Nickel)

Used for its sea water corrosion resistance and machine element work in this environment.

1.6mm/13.6kg

Hợp kim niken và niken

72E Nickel Chromium Molybdenum Alloy.

Nickel-Chromium-Molybdenum alloy used for its high strength and corrosion resistance.

1.6mm/13.6kg

06E Nickel

Used where dense NICKEL coatings are required.

1.6mm/15kg

73E Nickel Moly Chrome Iron (similar to Hastelloy C276)

73E is Similar to C276.  This material is well known for providing excellent corrosion resistance in a variety of aggressive media. The high molybdenum content imparts resistance to localized corrosion such as pitting.

1.6mm/13.6kg

75E Nickel/Aluminium Alloy

Produced specifically as an ARCSPRAY BONDING wire. Exotherms during spraying which produces very high bond strength coatings. Resistant to oxidation, high temperature and thermal cycling.

1.6mm/13.6kg

85E NiChrome 80/20

1.6mm/15kg

405/1T Nickel/ Aluminium Flamebond

A high performance Nickel/Aluminium for use in FLAMESPRAY BONDING as an alternative to 99E Molybdenum

3.17mm/13kg

Non-Slip Arctec

28E ARCTEC

Aluminium based wire that produced a reinforced aluminium coating, suitable for durable, non-slip applications. Tested for durability and with comparable corrosion protection to 01E Aluminium

2.3mm/60kg

TIN/ZINC

07E Tin/Zinc 70/30

TIN/ZINC alloys used for capacitor end connection and sprayed metal tooling applications.

2.0mm/150kg

08E Tin/Zinc 80/20

TIN/ZINC alloys used for capacitor end connection and sprayed metal tooling applications.A soft material that is easy to polish to create shiny, decorative coatings.

2.0mm/150kg

09E Tin/Zinc 60/40

TIN/ZINC alloys used for capacitor end connection and sprayed metal tooling applications. A soft material that is easy to polish to create shiny, decorative coatings.

2.0mm/150kg

19E Tin/Copper 97/3

Predominantly Tin based alloy used for bearing surfaces and electrical connections. A soft material that is easy to polish and create shiny coatings.

2.5mm/20kg

Zinc

02E Zinc

99.99% minimum purity ZINC. Coatings resistance to atmospheric and freshwater immersed corrosion.  Widely used for EFI/RFI shielding.

1.6mm 2.0mm 2.3mm/20kg

FeCrAl

78E Iron/ Chrome/Aluminium

Self bonding alloy especially suited to hot corrosion resistance in sulphurous atmospheres.

1.6mm/12.5kg

Stainless Steels

55E 18/5 Stainless Steel

Produces good corrosion resistant, low-shrink, work-hardening coatings. Ideal for thicker STAINLESS coating where cracking may be a problem.

1.6mm/15kg

80E 18/10 Stainless Steel

1.6mm/15kg

81E 312 Stainless Steel.

Produces good corrosion resistance with high shrink rates. Favoured for reinforced PTFE layers.

1.6mm/15kg

82E 308L Stainless Steel

Self bonding machinable alloy, somewhat softer than 80E.

1.6mm/15kg

84E 316 Stainless Steel

1.6mm/15kg

Babbitt

04E Babbitt

Tin based, BABBITT. Produces dense coatings ideal for high speed and heavy duty bearings.

2.0mm/10kg

 Copper & Bronzes

10E Aluminium Bronze

ALUMINIUM BRONZE alloy produces high tensile strength, low shrink wear resistant, dense coatings. Easily machinable and good for bearing surfaces and machine element work.

1.6mm/15kg

13E Brass (70/30)

COPPER/ZINC alloys producing solid dense coatings. Used for decorative work.

1.6mm/15kg

15E Phosphor Bronze

Easily machinable and good for bearing surfaces and machine element work. Also used for decorative coatings.

1.6mm/15kg

05E Copper

Pure COPPER, coatings give good electrical conductivity, used for RFI/EMI shielding and reclamation of mis-machined parts.

1.6mm/15kg

Arc Cored Wires

100T Nickel/Chrome/Boron

A nickel based coating which incorporates extremely hard particles in a hardened matrix. May be used in the ‘as sprayed’ state.

1.6mm/15kg

103T Iron/Chrome/Boron

Produces a hard, dense coating with almost no oxide content. Work hardens and grinds to an excellent finsh. The hardest of all iron based materials.

1.6mm/15kg

Chrome Steels

57E FM Chrome Steel

Generally used for low-shrink machine element work. Produces wear and corrosion resistant coatings with low tendency for cracking. Work-hardens.

1.6mm/15kg

60E 13% Chrome Steel

Best all-purpose steel for machine element work. Produces wear and corrosion resistant coatings with low tendancy for cracking. Work hardens.

1.6mm/15kg

65E High Chrome Manganese Steel

1.6mm/15kg

79E Ichrome

Self bonding one-step machinable alloy which can be easily ‘feather edged’ and milled without chipping.

1.6mm/15kg

87E Nickel/ Molybdenum

Produces low-shrink, work hardening coatings.

3.17mm/ 20-23kg